Liquid Applied Self-adhesive Waterproofing Membrane


Time:2019/7/19 16:26:51     Click Num:2461

Product overview

Reactive Self-adhesive Waterproofing Membrane adopts the construction method: wet-laid and pre-laid, wet-laid means lay the membranes on base course with cement mortar; pre-laid means just laying  the membranes on base course, and then pouring the concrete on the membranes.



Feature

1. Safe application

2. Easy to use

3. Safe and perfect overlapping

4. Ecological

5. Under normal storing and transporting conditions, the storage time should be at least one year.



Specification :

微信截图_20190807094559.png

PS: Every kind of product can be divided into single adhesive and double adhesive. 



Application:

Wet-laid waterproofing membranes are used for non-exposed waterproofing projects.



Notice:

1. Different products stacked separately.

2. Keep away from sun and rain, keep ventilation.

3. Storing temperature under 45℃.

4. Do not exceed 5 layers when the membranes flatted; and only single layer is allowed when the rolls are vertically placed.

5. No inclining and side crushing during transportation, and cover the products with felt if necessary.



Technical index:

(Perform standard: GB/T23457-2009 wet-laid self-adhesive waterproofing membrane)

 Item

Parameters

Polymer membrane

Polyester membrane

Type I

Type II

Type I

Type II

Soluble content/g/㎡)≥

3.0mm

---

2100

4.0mm

---

2900

Tensile property

Pull strength/N/50mm)≥

150

200

400

600

Tensile elongation at maximum pull strength/%

30

150

30

40

Tear strength/N

12

25

180

300

Heat resistance

70,2h

No displacement, flow, dripping

Low temperature flexibility/

-15

-25

-15

-25

No crack

Watertightness

0.3MPa,120min, watertight

Peel strength between membranes/N/50mm)≥

No treatment

1.0

Thermal aging

1.0

Oil permeability/number of sheets ≤

2

Holding power/min

15

Peel strength between membrane and cement mortar/N/50mm)≥

No treatment

2.0

Thermal aging

1.5

Peel strength between membrane and cement mortar after being immersed in water/N/mm)≥

1.5

Thermal aging

70,168h

Retention rate of tensile strength/% 

90

Retention elongation/%

80

 Low temperature flexibility

-13

-23

-13

-23

No crack

Thermal stability

Appearance

No wrinkleslidingflowing

Dimensional change/% 

2.0